Rozkład NO na beznośnikowych katalizatorach na bazie tlenkowych brązów.

master
dc.abstract.enThe literature part of the thesis includes characteristics of nitrogen oxides in terms of their impact on the environment and human health, description of the methods of the catalytic abatement of NOx emission and overview of the structures and properties of V-W oxide bronzes. The aim of this study was to determine the catalytic activity of V-W bronzes (W:V= 3,5:9) in the direct NO decomposition in 50-400oC temperature range.Nitric oxide decomposition was investigated in the gas mixtures containing 2% and 5% NO/He.The high NO conversion was stated in the whole range of temperatures. The results obtained reveals that NO adsorption is the only process proceeding at 50oC on the catalyst surface. The NO decomposition to N2 and N2O proceeds at 100-250oC temperature range and its rate and selectivity to nitrogen increases with the temperature increase. However, at temperature range 250 - 300oC for 5%NO/He and 250 - 350oC for 2%NO, N2 is the only product of NO decomposition. Above those temperatures nitrogen dioxide appears. Higher temperature of NO2 appearance for lower NO concentration reveals that atomic oxygen from NO decomposition participate in NO2 formation.Discussion of the results obtained allows to postulate N2O is formed as a result of the interaction of the NO(a) and N(a) on neighboring sites. However, NO2 is formed by interaction of the NO(a) and lattice oxygen atoms.pl
dc.abstract.otherCzęść literaturowa pracy składa się z charakterystyki poszczególnych tlenków azotu pod kątem ich oddziaływania na środowisko i zdrowie ludzkie, opisu metod katalitycznego ograniczania ich emisji i omówienia struktury i właściwości tlenkowych brązów V-W.Celem prezentowanej pracy było określenie aktywności tlenkowych brązów V-W (W:V= 3,5:9) w bezpośrednim rozkładzie NO w zakresie temperatur 50-400oC.Badano rozkład tlenku azotu w mieszaninach gazowych zawierających 5% i 2% NO/He. Stwierdzono wysoką konwersję tlenku azotu w całym zakresie temperaturowym.Otrzymane wyniki wskazują, że w obu przypadkach w temperaturze 50oC zachodzi tylko adsorpcja NO na powierzchni katalizatora. W temperaturach od 100-250oC następuje rozkład tlenku azotu do N2 i N2O z rosnącą ze wzrostem temperatury szybkością i selektywnością do azotu. Natomiast w temperaturach 250 do 300oC w przypadku 5%NO i w temperaturach 250 do 350oC w przypadku 2%NO jedynym produktem reakcji jest azot. Powyżej tych temperatur w produktach reakcji oprócz azotu pojawia się ditlenek azotu. Wyższa temperatura pojawiania się ditlenku azotu przy mniejszej zawartości tlenku azotu wskazuje, że tlen atomowy z rozkładu NO bierze udział w tworzeniu ditlenku azotu. Dyskusja otrzymanych wyników pozwala sądzić, że N2O powstaje na skutek oddziaływania NO(a) z N(a) zaadsorbowanym na sąsiednich centrach aktywnych. Natomiast NO2 tworzy się w wyniku oddziaływania tlenu sieciowego z zaadsorbowanym NO.pl
dc.affiliationWydział Chemiipl
dc.areaobszar nauk ścisłychpl
dc.contributor.advisorNajbar, Mieczysława - 130868 pl
dc.contributor.authorJaniga, Stanisławpl
dc.contributor.departmentbycodeUJK/WC3pl
dc.contributor.reviewerWesełucha-Birczyńska, Aleksandra - 132583 pl
dc.contributor.reviewerNajbar, Mieczysława - 130868 pl
dc.date.accessioned2020-07-15T17:23:04Z
dc.date.available2020-07-15T17:23:04Z
dc.date.submitted2011-06-28pl
dc.fieldofstudychemiapl
dc.identifier.apddiploma-57912-62600pl
dc.identifier.projectAPD / Opl
dc.identifier.urihttps://ruj.uj.edu.pl/xmlui/handle/item/172064
dc.subject.enNO decomposition, oxide bronzes V-Wpl
dc.subject.otherRozkład NO, tlenkowe brązy V-Wpl
dc.titleRozkład NO na beznośnikowych katalizatorach na bazie tlenkowych brązów.pl
dc.title.alternativeNO decomposition on unsupported catalysts based on oxide bronzes.pl
dc.typemasterpl
dspace.entity.typePublication
dc.abstract.enpl
The literature part of the thesis includes characteristics of nitrogen oxides in terms of their impact on the environment and human health, description of the methods of the catalytic abatement of NOx emission and overview of the structures and properties of V-W oxide bronzes. The aim of this study was to determine the catalytic activity of V-W bronzes (W:V= 3,5:9) in the direct NO decomposition in 50-400oC temperature range.Nitric oxide decomposition was investigated in the gas mixtures containing 2% and 5% NO/He.The high NO conversion was stated in the whole range of temperatures. The results obtained reveals that NO adsorption is the only process proceeding at 50oC on the catalyst surface. The NO decomposition to N2 and N2O proceeds at 100-250oC temperature range and its rate and selectivity to nitrogen increases with the temperature increase. However, at temperature range 250 - 300oC for 5%NO/He and 250 - 350oC for 2%NO, N2 is the only product of NO decomposition. Above those temperatures nitrogen dioxide appears. Higher temperature of NO2 appearance for lower NO concentration reveals that atomic oxygen from NO decomposition participate in NO2 formation.Discussion of the results obtained allows to postulate N2O is formed as a result of the interaction of the NO(a) and N(a) on neighboring sites. However, NO2 is formed by interaction of the NO(a) and lattice oxygen atoms.
dc.abstract.otherpl
Część literaturowa pracy składa się z charakterystyki poszczególnych tlenków azotu pod kątem ich oddziaływania na środowisko i zdrowie ludzkie, opisu metod katalitycznego ograniczania ich emisji i omówienia struktury i właściwości tlenkowych brązów V-W.Celem prezentowanej pracy było określenie aktywności tlenkowych brązów V-W (W:V= 3,5:9) w bezpośrednim rozkładzie NO w zakresie temperatur 50-400oC.Badano rozkład tlenku azotu w mieszaninach gazowych zawierających 5% i 2% NO/He. Stwierdzono wysoką konwersję tlenku azotu w całym zakresie temperaturowym.Otrzymane wyniki wskazują, że w obu przypadkach w temperaturze 50oC zachodzi tylko adsorpcja NO na powierzchni katalizatora. W temperaturach od 100-250oC następuje rozkład tlenku azotu do N2 i N2O z rosnącą ze wzrostem temperatury szybkością i selektywnością do azotu. Natomiast w temperaturach 250 do 300oC w przypadku 5%NO i w temperaturach 250 do 350oC w przypadku 2%NO jedynym produktem reakcji jest azot. Powyżej tych temperatur w produktach reakcji oprócz azotu pojawia się ditlenek azotu. Wyższa temperatura pojawiania się ditlenku azotu przy mniejszej zawartości tlenku azotu wskazuje, że tlen atomowy z rozkładu NO bierze udział w tworzeniu ditlenku azotu. Dyskusja otrzymanych wyników pozwala sądzić, że N2O powstaje na skutek oddziaływania NO(a) z N(a) zaadsorbowanym na sąsiednich centrach aktywnych. Natomiast NO2 tworzy się w wyniku oddziaływania tlenu sieciowego z zaadsorbowanym NO.
dc.affiliationpl
Wydział Chemii
dc.areapl
obszar nauk ścisłych
dc.contributor.advisorpl
Najbar, Mieczysława - 130868
dc.contributor.authorpl
Janiga, Stanisław
dc.contributor.departmentbycodepl
UJK/WC3
dc.contributor.reviewerpl
Wesełucha-Birczyńska, Aleksandra - 132583
dc.contributor.reviewerpl
Najbar, Mieczysława - 130868
dc.date.accessioned
2020-07-15T17:23:04Z
dc.date.available
2020-07-15T17:23:04Z
dc.date.submittedpl
2011-06-28
dc.fieldofstudypl
chemia
dc.identifier.apdpl
diploma-57912-62600
dc.identifier.projectpl
APD / O
dc.identifier.uri
https://ruj.uj.edu.pl/xmlui/handle/item/172064
dc.subject.enpl
NO decomposition, oxide bronzes V-W
dc.subject.otherpl
Rozkład NO, tlenkowe brązy V-W
dc.titlepl
Rozkład NO na beznośnikowych katalizatorach na bazie tlenkowych brązów.
dc.title.alternativepl
NO decomposition on unsupported catalysts based on oxide bronzes.
dc.typepl
master
dspace.entity.type
Publication
Affiliations

* The migration of download and view statistics prior to the date of April 8, 2024 is in progress.

Views
5
Views per month
Views per city
Wroclaw
2
Dublin
1
Warsaw
1

No access

No Thumbnail Available